Abstract
Pure graphene is known as the strongest material ever discovered. However, the unavoidable defect formation in the fabrication process renders the strength of defective graphene much lower (~14%) than that of its perfect counterpart. By means of density functional theory computations, we systematically explored the effect of gas molecules (H2, N2, NH3, CO, CO2 and O2) adsorption on the mechanical strength of perfect/defective graphene. The NH3 molecule is found to play a dominant role in enhancing the strength of defective graphene by up to ~15.6%, while other gas molecules decrease the strength of graphene with varying degrees. The remarkable strength enhancement can be interpreted by the decomposition of NH3, which saturates the dangling bond and leads to charge redistribution at the defect site. The present work provides basic information for the mechanical failure of gas-adsorbed graphene and guidance for manufacturing graphene-based electromechanical devices.
Similar content being viewed by others
Introduction
Graphene, as a single-layer of sp2-hybridized carbon atoms arranged in a honeycomb lattice, has demonstrated many unique physical and chemical properties1. In particular, pristine graphene possesses exceptionally high stiffness and strength and is known as the strongest two-dimensional material, which inspires the explorations of a wide range of potential applications such as lightweight and high strength materials and composites2,3,4,5,6,7. However, the existing experiments8,9,10 reported rather different values of in-plane stiffness for graphene, partly due to the different experimental conditions. Specifically, the emergence of defects in the graphene (D-graphene) lattice is ubiquitous, due to fabrication processes11,12,13 and the environmental conditions to which the graphene sheets are exposed14,15,16. Such defects would inevitably degrade the ideal strength of graphene17, resulting in the reduction of its breaking strength to only ~14%. In this context, how to improve the stiffness of D-graphene is of great importance for its applications in graphene-based nanoelectromechanical devices. Moreover, the presence of defects is also essential for the desired functionality, for example, for the applications in biodevices and DNA-decorated graphene18,19.
Noticeably gas adsorption on nanomaterials20,21,22,23,24,25,26,27 is attracting great interest because provides an effective method to control the spatial organization of adsorbates that are known to modify the chemical and electronic properties of the host materials. For example, Schedin et al.28 experimentally demonstrated that micrometre-size sensors made from graphene can detect individual gas molecules adsorbed on graphene. Inspired by this exciting experimental finding, Leenaerts et al.29 studied the optimal adsorption position and orientation of NH3, CO, NO2 and NO on a graphene substrate by means of density functional theory (DFT) computations and pointed out that the dramatic change of the electronic properties after the adsorption of the gas molecule contributes to the high performance of graphene sensors. So far, a considerable number of theoretical and experimental studies have been performed to investigate the effect of adsorbates on the structural and electronic properties of host materials. However, the effect of gas adsorption on the mechanical properties has been rarely studied. Unveiling the effect of gas molecule adsorption on the mechanical properties of the graphene layer would help us understand this issue, which is important for its applications in flexible electronic nanodevices and other related fields.
In this paper, we performed a systematic study of gas adsorption on the perfect/defective graphene layer to evaluate the mechanical strength change. Many common gases, namely H2, N2, NH3, CO, CO2 and O2, have been considered due to their importance to environmental and industrial applications. We first investigate the structural and mechanical properties of the perfect graphene (P-graphene) with adsorbed gas molecules. Then, the change of ideal strain for the D-graphene upon gas molecule adsorption is investigated. Finally, the mechanisms behind the strength change are analysed to gain more insights into the effects of adsorbed molecules on the mechanical properties of D-graphene.
Computational Method
Our spin polarized DFT computations were performed by utilizing Viena ab intio simulation package (VASP) code30,31 with the implemented projector augment wave (PAW) method32,33. The generalized gradient approximation in the Perdew-Burke-Ernzerhof form (GGA-PBE)34 was used to describe the exchange-correlation for electrons. A dispersion correction to the total energy (DFT-D3 method)35 was employed to simulate the long-range van der Waals interaction. The plane-wave energy cutoff was set to 400 eV for geometry optimization and to 500 eV for static electronic structure calculations. To study two-dimensional (2D) systems under the periodic boundary conditions, a vacuum layer with a thickness of at least 20 Å was used to avoid the interaction between periodic images. All the geometry structures were fully relaxed until energy and force were converged to 1.0−5 eV and 0.005 eV/Å, respectively. A 5 × 5 × 1 and 17 × 17 × 1 Monkhorst–Pack k-point sampling was used for geometry optimizations and static electronic structure calculations, respectively. The adsorption energy (Ead) of a gas molecule on graphene layer was obtained by the following equation: Ead = E(gas+G) − (EG + Egas), where E(gas+G), EG and Egas are the total energies of the gas adsorbed graphene system, graphene and the adsorbed gas molecule, respectively. According to this definition, a more negative Ead value indicates a more favourable adsorption.
The strain36,37 was added by changing the lattice parameters a, which is determined by the expression a = a0 (1 + ε). Here, a0 is the equilibrium lattice constants of graphene at 0% strain. The values of ε increased in steps of 0.4% until the graphene sheet fractured and the strain-stress relation was obtained. To eliminate the artificial effect of the out-of-plane thickness of the simulation box on the stress, we employed the second Piola–Kirchhoff stress37,38 to express the 2D forces with units of N/m. In order to lift the constraints imposed by periodic boundary conditions39, a 3 × 3 supercell was used for all the calculations. Note that only a single vacancy in each supercell was considered in order to reduce the complexity.
Results and Discussion
Structural and mechanical properties of the perfect graphene with adsorbed gas molecules
First, we search for the lowest-energy configuration when a gas molecule is adsorbed on P-graphene. To find the most favourable position for gas adsorption, we place the single gas molecule above the graphene layer at different distances and orientations. After full optimization, the obtained configurations are compared and the energetically most favourable states are selected for further discussions.
As a representative, the case for NH3 is presented in Fig. 1. The NH3 molecule prefers to locate in the hexagon center (Fig. 1a) and the calculated distance (see Table 1) between the NH3 molecules and graphene is 2.84 Å. The computed adsorbent-graphene distances, adsorption energies and magnetic moments for other gas molecules (H2, N2, CO, CO2 and O2) are given in the Table 1. In the equilibrium, all these gas molecules are physically adsorbed on graphene with a distance between 2.68–3.32 Å. However, only the adsorption of H2, NH3 and O2 is exothermic while others are not favoured energetically and only O2 adsorbed system is magnetic.
Before studying the strain effect on the gas-adsorbed graphene, we investigated the strain-stress relationship in the P-graphene as shown in the Fig. 2a. In an attempt to evaluate the “minimum” ideal strain for graphene, both armchair and zigzag directions seem possible to be chosen. However, a previous report40 revealed that the armchair direction possesses lower ideal strain than the zigzag direction, since it is parallel to the carbon-carbon bond which dominates the mechanics of graphene41. Therefore, only the armchair direction is considered in our calculations. Our computations show that the P-graphene sheet can sustain a maximum stress up to ~32 N/m and its structure does not fracture even when the strain exceeds 30% (Fig. 2b), which is in consistent with previous theoretical work40.
However, the adsorption of a single gas molecule on the top of graphene sheet can significantly decrease its mechanical strength (Fig. 2b). The largest reduction derives from the adsorption of NH3, where the fracture point drops to only 15.6% relative to that of P-graphene (>30% of the fracture point). These results well explain why the synthesized graphene layers exhibit relatively low intrinsic strength (~15% of the fracture point) under realistic experimental conditions, which include gas exposure.
Structural and mechanical properties of the defective graphene with adsorbed gas molecules
Normally, a material’s ideal (intrinsic) strength can be traced down to its bond strength42. The bond strength, in principle, can be greatly affected by the amount of charge in the bond. Removing one atom from the nanosheet will have a significant impact on the charge distribution of the layer, resulting in weakening the bond strength. As a result, the ideal strength of the material would be reduced. For example, the P-graphene is able to sustain an ideal strain above 30% (Fig. 2a), while the unavoidable defects in fabrication process (e.g. carbon atom vacancies) can significantly affect its strength, i.e. decreasing to only 14.8% (Fig. 3a). The introduction of foreign atoms in the defect sites of graphene brings new electron to interact with the dangling bonds, which therefore affect the bond strength and thus change the strain of the host materials. Motivated by this rationale, we explore the gas adsorption on D-graphene in order to modulate the ideal strain for D-graphene as well as shed new lights on the underlying mechanism.
Our computations show that the adsorption of H2, N2, CO, CO2 or O2 molecules makes the critical strain for D-graphene decrease by 0.4~2.0% (Fig. 3b). The most significant reduction comes from the CO or CO2 adsorbed D-graphene, where its breaking strain drops to only 12.8%. However, there is a shining exception: the NH3 dissociative adsorption enhances the ideal strain of D-graphene by approximately 1%, i.e. to 15.6%. Compared with the gas adsorption on the P-graphene, all the gas adsorptions turn to be energetically favourable on the D-graphene sheet (Table 2) and the remarkable high Ead (9.083 eV) for NH3 also indicates that it dissociates on the D-graphene sheet. Furthermore, all of the six gas-adsorbed systems become magnetic.
With regard to the NH3 adsorption on defective graphene, experimentally it has been demonstrated that the NH3 molecule can easily dissociate on this host layer43. To validate the possibility of gas decomposition, we performed the nudged elastic band (NEB)44 DFT calculations for the NH3 + D-graphene system at different strains, as shown in Fig. 4. By computing the transition states, we find that the NH3 decomposition needs to overcome an energy barrier (Ea) of 0.5 eV for the strain-free D-graphene, while the Ea value decreases as the strain increases. As a 0.5 eV energy barrier is not sufficient to hinder the NH3 decomposition, it is reasonable to expect the NH3 decomposition to occur without stain, while the finite strains can accelerate this process.
The high possibility of NH3 decomposition on defective graphene, as revealed by our NEB calculations, is further verified by the optimized structural configuration of NH3 + D-graphene system (Fig. 5). The NH3 decomposition happens above the D-graphene sheet. When the strain is less than 12.8%, the NH3 molecule is dissociated into NH2 and H, NH2 is physisorbed at the carbon atom with a dangling bond, while H bonds to a neighbouring carbon atom (-c-H) (Fig. 5a–c). This dissociative NH3 adsorption induces obvious corrugation on the D-graphene layer (Fig. 5b) due to the strong electron coupling between the adsorbed species and the D-graphene sheet.
Interestingly, when the D-graphene is further stretched with a strain greater than 12.8%, the NH2 is further dissolved into NH and -c-H (Fig. 5d). Note that the H fragment plays a dominant role in saturating the dangling bond at the defect site, which would affect the charge distribution and strengthen the carbon bond (the neighbouring bond length reduces to 1.40 Å). As a result, the ideal strain for D-graphene is enhanced by the dissociative adsorption of NH3. Furthermore, we have also checked the structure for H2/N2/CO/CO2/O2 + D-graphene system, but no gas decomposition is found. Thus, the experimentally observed difference on the mechanical strength can be attributed to the differing impact of different gas adsorption at the defected site of graphene.
Finally, we examine the relationship between the stress and the strain for the NH3 + D-graphene system (Fig. 5e). The yield point of NH3 adsorbed graphene is at 12% strain. Before this point, it is in the elastic range where the deformation is reversible and the stretched layer can return to its original geometry when the tension is released. Further extension after the yield point would induce an irreversible plastic deformation and the 2D structure will eventually rupture (see the structural change in Fig. 5d) after reaching the critical breaking strain of 15.6%.
Conclusion
We systematically investigated the ideal strength for P-/D-graphene adsorbed by several common gas molecules including H2, N2, NH3, CO, CO2 and O2 by means of DFT computations. All the gas adsorption on P-graphene can significantly reduce its breaking strain and the similar trend is also revealed for D-graphene that adsorbed by H2, N2, CO, CO2 and O2. Most importantly, the NH3 adsorption on D-graphene can significantly enhance its ideal strain to 15.6% and the fundamental mechanism has been analysed in terms of NH3 dissociation. These results supply useful information for the ideal strength of gas adsorbed graphene system and provide guidance to the fabrication of graphene-based electromechanical devices.
Additional Information
How to cite this article: Ma, F. et al. Anomalous Enhancement of Mechanical Properties in the Ammonia Adsorbed Defective Graphene. Sci. Rep. 6, 33810; doi: 10.1038/srep33810 (2016).
References
Singh, V. et al. Graphene based materials: Past, present and future. Progress in Materials Science 56, 1178–1271 (2011).
Jiao, Y. et al. Graphene-covered perovskites: an effective strategy to enhance light absorption and resist moisture degradation. RSC Advances 5, 82346–82350 (2015).
Ma, F. et al. Single Layer Bismuth Iodide: Computational Exploration of Structural, Electrical, Mechanical and Optical Properties. Scientific Reports 5, 17558 (2015).
Odedairo, T. et al. Nanosheets Co3O4 Interleaved with Graphene for Highly Efficient Oxygen Reduction. ACS Applied Materials & Interfaces 7, 21373–21380 (2015).
Du, A. et al. Hybrid Graphene and Graphitic Carbon Nitride Nanocomposite: Gap Opening, Electron–Hole Puddle, Interfacial Charge Transfer and Enhanced Visible Light Response. J. Am. Chem. Soc. 134, 4393–4397 (2012).
Du, A. & Smith, S. C. Electronic Functionality in Graphene-Based Nanoarchitectures: Discovery and Design via First-Principles Modeling. J. Phys. Chem. Lett. 2, 73–80 (2011).
Du, A. In silico engineering of graphene-based van der Waals heterostructured nanohybrids for electronics and energy applications. Wiley Interdisciplinary Reviews: Computational Molecular Science 6, 551–570 (2016).
Metten, D., Federspiel, F., Romeo, M. & Berciaud, S. All-Optical Blister Test of Suspended Graphene Using Micro-Raman Spectroscopy. Physical Review Applied 2, 054008 (2014).
Lee, J.-U., Yoon, D. & Cheong, H. Estimation of Young’s Modulus of Graphene by Raman Spectroscopy. Nano Lett. 12, 4444–4448 (2012).
Lin, Q.-Y. et al. Stretch-Induced Stiffness Enhancement of Graphene Grown by Chemical Vapor Deposition. ACS Nano 7, 1171–1177 (2013).
McAllister, M. J. et al. Single Sheet Functionalized Graphene by Oxidation and Thermal Expansion of Graphite. Chem. Mater. 19, 4396–4404 (2007).
Schniepp, H. C. et al. Functionalized Single Graphene Sheets Derived from Splitting Graphite Oxide. The Journal of Physical Chemistry B 110, 8535–8539 (2006).
Stankovich, S. et al. Stable aqueous dispersions of graphitic nanoplatelets via the reduction of exfoliated graphite oxide in the presence of poly(sodium 4-styrenesulfonate). Journal of Materials Chemistry 16, 155–158 (2006).
Kim, K. S. et al. Large-scale pattern growth of graphene films for stretchable transparent electrodes. Nature 457, 706–710 (2009).
Park, S. & Ruoff, R. S. Chemical methods for the production of graphenes. Nat. Nanotechnol. 4, 217–224 (2009).
Bae, S. et al. Roll-to-roll production of 30-inch graphene films for transparent electrodes. Nat. Nanotechnol. 5, 574–578 (2010).
Zandiatashbar, A. et al. Effect of defects on the intrinsic strength and stiffness of graphene. Nat. Commun. 5, 3186 (2014).
Ang, P. K., Chen, W., Wee, A. T. S. & Loh, K. P. Solution-Gated Epitaxial Graphene as pH Sensor. J. Am. Chem. Soc. 130, 14392–14393 (2008).
Cohen-Karni, T., Qing, Q., Li, Q., Fang, Y. & Lieber, C. M. Graphene and Nanowire Transistors for Cellular Interfaces and Electrical Recording. Nano Lett. 10, 1098–1102 (2010).
Leenaerts, O., Partoens, B. & Peeters, F. M. Adsorption of H2O,MH3,CO,NO2 and NO on graphene: A first-principles study. Phys. Rev. B 77, 125416 (2008).
Kou, L., Du, A., Chen, C. & Frauenheim, T. Strain engineering of selective chemical adsorption on monolayer MoS2. Nanoscale 6, 5156–5161 (2014).
Jijun, Z., Alper, B., Jie, H. & Jian Ping, L. Gas molecule adsorption in carbon nanotubes and nanotube bundles. Nanotechnology 13, 195 (2002).
Huang, B. et al. Adsorption of Gas Molecules on Graphene Nanoribbons and Its Implication for Nanoscale Molecule Sensor. J. Phys. Chem. C 112, 13442–13446 (2008).
Li, Y., Zhou, Z. & Zhao, J. Transformation from chemisorption to physisorption with tube diameter and gas concentration: Computational studies on NH3 adsorption in BN nanotubes. J. Chem. Phys. 127, 184705 (2007).
Zhao, S., Xue, J. & Kang, W. Gas adsorption on MoS2 monolayer from first-principles calculations. Chemical Physics Letters 595–596, 35–42 (2014).
Yue, Q., Shao, Z., Chang, S. & Li, J. Adsorption of gas molecules on monolayer MoS2 and effect of applied electric field. Nanoscale Research Letters 8, 1–7 (2013).
Terranova, M. L., Orlanducci, S. & Rossi, M. Carbon Nanomaterials for Gas Adsorption (CRC Press, 2012).
Schedin, F. et al. Detection of individual gas molecules adsorbed on graphene. Nat. Mater. 6, 652–655 (2007).
Leenaerts, O., Partoens, B. & Peeters, F. M. Adsorption of H2O, NH3, CO, NO2 and NO on graphene: A first-principles study. Phys. Rev. B 77, 125416 (2008).
Kresse, G. & Furthmüller, J. Efficiency of ab initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comput. Mater. Sci. 6, 15–50 (1996).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Physical Review B 59, 1758–1775 (1999).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized Gradient Approximation Made Simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Grimme, S. Semiempirical GGA-type density functional constructed with a long-range dispersion correction. J. Comput. Chem. 27, 1787–1799 (2006).
Peng, Q., Ji, W. & De, S. Mechanical properties of graphyne monolayers: a first-principles study. Physical Chemistry Chemical Physics 14, 13385–13391 (2012).
Peng, Q., Ji, W. & De, S. Mechanical properties of the hexagonal boron nitride monolayer: Ab initio study. Comput. Mater. Sci. 56, 11–17 (2012).
Peng, Q. et al. Mechanical degradation of graphene by epoxidation: insights from first-principles calculations. Physical Chemistry Chemical Physics 17, 19484–19490 (2015).
Topsakal, M., Aktürk, E. & Ciraci, S. First-principles study of two- and one-dimensional honeycomb structures of boron nitride. Phys. Rev. B 79, 115442 (2009).
Cao, G. Atomistic Studies of Mechanical Properties of Graphene. Polymers 6, 2404 (2014).
Lopez-Polin, G. et al. Increasing the elastic modulus of graphene by controlled defect creation. Nat Phys 11, 26–31 (2015).
Si, C., Duan, W., Liu, Z. & Liu, F. Electronic Strengthening of Graphene by Charge Doping. Phys. Rev. Lett. 109, 226802 (2012).
Mattson, E. C. et al. Exploring Adsorption and Reactivity of NH3 on Reduced Graphene Oxide. J. Phys. Chem. C 117, 10698–10707 (2013).
Sheppard, D., Xiao, P., Chemelewski, W., Johnson, D. D. & Henkelman, G. A generalized solid-state nudged elastic band method. J. Chem. Phys. 136, 074103 (2012).
Acknowledgements
We acknowledge generous grants of high-performance computer time from computing facility at Queensland University of Technology and Australian National Facility. A.D. greatly appreciates the Australian Research Council QEII Fellowship (DP110101239) and financial support of the Australian Research Council under Discovery Project (DP130102420). The first author (F.M.) also acknowledges the support through the CSIRO top-up scholarship. A.B. thanks CSIRO for support through the Julius Career Award. Z.C. thanks the financial supports by Department of Defense (Grant W911NF-15-1-0650).
Author information
Authors and Affiliations
Contributions
F.M. and A.D. conceived the idea. F.M. and Y.J. performed the calculations. F.M., Y.G., A.B., Y.C., Z.C. and A.D. contributed to the analysis of the results and to the writing of the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Ma, F., Jiao, Y., Gu, Y. et al. Anomalous Enhancement of Mechanical Properties in the Ammonia Adsorbed Defective Graphene. Sci Rep 6, 33810 (2016). https://doi.org/10.1038/srep33810
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep33810