A Mg–Al–Nd alloy produced via a powder metallurgical route

https://doi.org/10.1016/j.msea.2009.03.073Get rights and content

Abstract

A Mg–5 wt.%Al–2 wt.%Nd alloy has been prepared by a powder metallurgical route using a blend of two dissimilar alloy powders. The initial consolidation of the powders was achieved through a single equal channel angular extrusion pass at 150 °C. After heat treatment at temperatures between 420 °C and 530 °C, it was possible to produce a microstructure that consisted of a uniform distribution of Al3Nd and Al11Nd3 precipitates in a magnesium matrix. These precipitates displayed distinct orientation relationships with the matrix. The size and shape of the precipitates depended on the heat treatment temperature and time.

Introduction

Rare Earth (RE) additions to magnesium, either alone or in conjunction with aluminium, have become increasingly popular in recent years for applications at elevated temperatures where they impart improved creep resistance. Whilst several creep resistant alloys have recently been developed for both low pressure/gravity and high pressure die cast (HPDC) processing routes, the most popular remains AE42, which is solely a HPDC alloy and has limited creep resistance above 150 °C. Being a HPDC alloy, there are limited opportunities to use heat treatment to improve the elevated temperature behaviour. The improvements, such as they are, in the creep properties of these Mg–Al–RE alloys over the Mg–Al–Zn alloys such as AZ91 are linked to the formation of Al–RE phases, primarily Al11RE3 in AE42 [1]. However, the deleterious Mg17Al12 phase may also form during solidification if there is excess aluminium in the alloy, or as a transformation product after prolonged exposure to elevated temperatures during service. This latter effect is particularly prevalent in alloys based on cerium-based mischmetal, but can be alleviated by increasing the Nd level at the expense of the La, in which case the primary intermetallic phase becomes the more stable Al2RE [2].

An alternative net shape process for smaller components, based on powder metallurgy and heat treatment, is ‘interference hardening’. This process, which alloys the elements together in the solid state, was first described by Busk and Leontis in 1950 and involved the high strain ratio simultaneous extrusion of Mg–0.3 wt.%Zr and 12 wt.% Mg–Al eutectic powder particles [3]. The extrusion of the separated elements resulted in a fully dense microstructure that, upon heat treatment, transformed into a Mg–Al matrix containing a continuous distribution of AlZr3 precipitates. If this alloy had been processed via a molten route the aluminium would have formed massive insoluble intermetallics with the zirconium during solidification, resulting in a microstructure that would be impossible to fully homogenise, assuming heat treatment was possible, and therefore the uniform distribution of precipitates throughout the matrix would be unattainable. The principles of interference hardening and the criteria for the selection of appropriate powder compositions have been described elsewhere [4]. This method requires the different species of metal powder to be highly deformed plastically during consolidation in order to ensure good interparticle bonding, and hence the formation of adequate diffusion paths. Indeed, the patent based on this method recommends extrusion ratios in excess of 30:1 (equivalent to an imposed strain of 3.4), which leads to some severe restrictions on the final size of any component that may be produced by this method [5]. Equal Channel Angular Pressing (ECAP) is an alternative technique that provides high strains, of the order of 1.15, on the billet per pass. A major advantage of this technique is that the strain can be imposed without a change in the cross sectional dimensions, and hence multiple passes may be undertaken without dimensional change to further accumulate strain. In addition, the strain induced is uniform across the cross section of the billet while the required high extrusion ratio and friction in conventional extrusion lead to non-uniform strain distribution within the extruded billet [6], [7], [8]. This technique has previously been shown to adequately consolidate both titanium and aluminium powders [9], [10], [11] and the authors have recently demonstrated that dense magnesium powder compacts are possible [12].

Interference hardening opens up possibilities for the microstructural manipulation of several magnesium alloy compositions that would otherwise be impossible to precipitation harden due to the thermal stability of the solidification compounds and/or the selection of the casting process. One such alloy system is that based on Mg–Al–RE compositions. In this paper, preliminary results, from a Mg–Al–Nd alloy, demonstrating the viability of this technique are reported.

Section snippets

Experimental

Two target alloy compositions were investigated: Mg–5 wt.%Al–2 wt.%Nd and Mg–3.7 wt.%Al–2 wt.%Nd. The majority alloying element, which was the aluminium, was added in two forms: Pure aluminium powder (<40 μm) and a 67 wt.%Mg–33 wt.%Al composition with a eutectic (Mg–Mg17Al12) microstructure. The eutectic material was added as both a coarsely (<600 μm) and finely (<200 μm) ground powder. The ternary element in the system was neodymium, contained in the second powder component, a Mg–Nd solid solution,

Results

The consolidation using ECAP resulted in a billet of circular cross section. Density was measured after compaction, and again after heat treatment (see Table 1). Clearly, there is some variability from one processing run to another, with alloys 1–5 being produced from the same starting material (based on Al powder) and under the same pressing conditions but showing relative densities of between 98% and 100% (four of the five, however, are in excess of 99.5%). Multiple ECAP passes (alloy 6) do

Discussion

The direct consolidation of the powder mixtures using ECAP produced green compacts with relative densities in excess of 98%. The use of pure Al powder was beneficial for the initial consolidation, with the brittle, and therefore less deformable, eutectic material leading to slightly lower densities. It should be noted, however, that in all but one instance the relative densities were in excess of 99% and the difference between 99% and 99.9% relative density may be considered to be within

Summary

Dissimilar alloy powders, a Mg–Nd solid solution and either pure Al or a Mg–Mg17Al12 alloy, have been blended together and consolidated to near full density using a single ECAP pass with back pressure at 150 °C. After heat treatment at 420 °C for periods of several hours, the microstructure consisted of a magnesium matrix and a homogeneous distribution of 20–30 nm rod and/or plate-shaped precipitates of Al3Nd and Al11Nd3 with specific orientation relationships with the surrounding matrix. This is

Acknowledgements

The authors wish to thank Dr. M.A. Gibson of CAST CRC for providing the Mg–Nd alloy from which one of the powders was prepared. M. Moss was supported through a scholarship from the ARC Centre of Excellence for Design in Light Metals.

References (15)

  • A. Shan et al.

    Scripta Materialia

    (1999)
  • R. Lapovok et al.

    Scripta Materialia

    (2008)
  • K. Xia et al.

    Scripta Materialia

    (2005)
  • R. Lapovok et al.

    Materials Science and Engineering A

    (2008)
  • G. Moreau et al.

    Journal of Nuclear Materials

    (1971)
  • C.J. Bettles

    Materials Science and Engineering A

    (2003)
  • Q.M. Amir et al.

    Canadian Metallurgical Quarterly

    (1995)
There are more references available in the full text version of this article.

Cited by (15)

  • Production of Magnesium and Magnesium Alloy Powders

    2018, Handbook of Non-Ferrous Metal Powders: Technologies and Applications, Second Edition
  • The effect of processing routes on the structure and properties of magnesium-TiNi composites

    2012, Materials Science and Engineering: A
    Citation Excerpt :

    Typically, these conventional techniques are not preferred because the oxide layers that form on the exposed powder surfaces cannot be broken, and these layers have a tendency to prevent sufficient sintering. Moreover, processes such as hot extrusion, swaging and equal channel angular pressing (ECAP) [11], which make use of the simultaneous application of deformation and heat, are effective ways for magnesium composite production because they create increased fresh metallic surface area, which is then available for sintering, by breaking the oxide films via high deformation rates. Ceramics, such as oxides, nitrides, borides and carbides, i.e., Al2O3, TiN, TiB2, SiC, B4C, are usually used for the reinforcement of magnesium and its alloys [8].

  • Microstructure and elevated temperature mechanical properties of ECAPed Mg-15Al-xNd alloys

    2016, Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment
View all citing articles on Scopus
View full text