Abstract.
Boron powder, finely ground in a tungsten carbide ball mill in an ammonia atmosphere, has been annealed at 1200 °C in flowing nitrogen to produce small quantities of cylindrical BN nanotubes, both as isolated individuals and grouped into ropes. Thick-walled conical BN tubes are abundant in specimens annealed for longer times, and their growth was catalysed once WC debris was converted into W metal particles. Some catalytic effect of small W nanoparticles could be necessary for nanotube formation, though no tip particles have been imaged here. Given the low temperature of mechanical milling and annealing, BN growth must involve surface diffusion and solid-state reconfiguration. It could be possible to engineer desirable physical and chemical properties by exploiting the variation in cylindrical versus conical BN structures as a function of annealing time.
Author information
Authors and Affiliations
Additional information
Received: 19 December 2001 / Accepted: 3 April 2002 / Published online: 19 July 2002
RID="*"
ID="*"Corresponding author. Fax: +61-2/6125-8253, E-mail: john.fitzgerald@anu.edu.au
Rights and permissions
About this article
Cite this article
Fitz Gerald, J., Chen, Y. & Conway, M. Nanotube growth during annealing of mechanically milled Boron . Appl Phys A 76, 107–110 (2003). https://doi.org/10.1007/s00339-002-1441-5
Issue Date:
DOI: https://doi.org/10.1007/s00339-002-1441-5